Division of Bio-Resource, Paper & Coatings Technology School of Industrial Technology, Universiti Sains Malaysia, 11800 Penang, Malaysia
The dependence of peel strength and shear strength of epoxidized natural rubber (ENR-25)-based pressure sensitive adhesive on molecular weight and rate of testing was investigated using coumarone-indene as the tackifying resin. Toluene and polyethylene terephthalate (PET) were used as the solvent and substrate respectively throughout the study. A SHEEN hand coater was used to coat the adhesive on the substrate at a coating thickness of 120 μm. All the adhesion properties were determined by a Llyod Adhesion Tester operating at different rates of testing. Result shows that peel strength and shear strength increases up to an optimum molecular weight of 6.5×10 of ENR 25. For peel strength, the observation is attributed to the combined effects of wettability and mechanical strength of rubber at the optimum molecular weight, whereas for the shear strength, it is ascribed to the increasing amount of adhesive present in the coating layer which enhances the shear resistance of the adhesive. Peel strength and shear strength also increases with increase in rate of testing, an observation which is associated to the viscoeslastic response of the adhesive. Differential scanning calorimetry (DSC) and Fourier transform infrared spectroscopy (FTIR) study confirms the miscibility of tackifier and the ENR 25.
►Elucidation of adhesion property of epoxidized natural rubber (ENR 25).►Correlation of peel and shear strength with molecular weight and rate of testing.►Confirmation of miscibility of tackifier and ENR 25 by DSC and FTIR study.►Applicability of Fox Equation in ENR 25/coumarone-indene resin system.
Keywords: A. Elastomers and rubber; G. Thermal analysis; I. Adhesion
本站所有信息与内容,版权归原作者所有。网站中部分新闻、文章来源于网络或会员供稿,如读者对作品版权有疑议,请及时与我们联系,电话:025-85303363 QQ:2402955403。文章仅代表作者本人的观点,与本网站立场无关。转载本站的内容,请务必注明"来源:林中祥胶粘剂技术信息网(www.adhesive-lin.com)".
©2015 南京爱德福信息科技有限公司 苏ICP备10201337 | 技术支持:南京联众网络科技有限公司