Preparing method for phenolic resin adhesive for wood
(木材用酚醛树脂胶黏剂的制备方法)
Inventor(s): LI XIAOMING
Application number: CN20151817033 20151123
Abstract of CN105315936 (A):
The invention provides a preparing method for phenolic resin adhesive for wood. The preparing method includes the following steps that 1, boron carbide powder is added into absolute ethyl alcohol after being dried and stirred to obtain mixed liquid, the mixed liquid is added into an ethyl alcohol solution of KH570, the mixed solution is stirred for reacting after the ph value is adjusted and then stands at the room temperature, and drying is carried out after suction filtration to obtain modified boron carbide for use; 2, by weight, 100 parts of phenol and 70-80 parts of a formaldehyde solution are added into a stirring kettle and uniformly stirred, then 10-15 parts of composite catalysts are added, after heating, a reaction is carried out at the constant temperature under stirring, 2-7 parts of an acid catalyst is added into the stirring kettle, a reaction continues to be carried out at the constant temperature under stirring, 9-10 parts of polyarylester and 5-6 parts of the modified boron carbide are added into the stirring kettle, and a reaction continues to be carried out at the constant temperature under stirring; 3, after the reaction is stopped, the product stands, is placed in deionized water to be washed, and is dehydrated through reduced pressure distillation, dehydration is stopped when the temperature rises to 105 DEG C, and the phenolic resin adhesive for wood is obtained after the product is naturally cooled to the room temperature. The adhesive prepared through the method is good in abrasive resistance, heat resistance and flame retardancy.
本站所有信息与内容,版权归原作者所有。网站中部分新闻、文章来源于网络或会员供稿,如读者对作品版权有疑议,请及时与我们联系,电话:025-85303363 QQ:2402955403。文章仅代表作者本人的观点,与本网站立场无关。转载本站的内容,请务必注明"来源:林中祥胶粘剂技术信息网(www.adhesive-lin.com)".
©2015 南京爱德福信息科技有限公司 苏ICP备10201337 | 技术支持:建站100